Pengaruh proses annealing terhadap angka kekerasan dan struktur mikro pada komponen thrust washer differential
Abstrak (Abstracts)

Annealing merupakan proses heat treatment yang dilakukan dengan tujuan untuk melunakkan bahan logam, khususnya baja karbon. Berdasarkan studi kasus ditemukan bahwa komponen thrust washer differential pada unit dump truck-machine model CWB6BLLDN2 mengalami kegagalan. Kegagalan komponen disebabkan tumbukan/hentakan oleh gear differential di dalam differential case. Pecahnya thrust washer tersebut diakibatkan oleh sifat komponen yang tidak mampu terhadap impack load (hentakan). Proses annealing menggunakan variasi temperatur sebesar 825 °C, 875 °C, 925 °C, dan 975 °C. Metode pendinginan yang digunakan adalah pendinginan di dalam tungku pemanas. Pengujian kekerasan menggunakan pengujian Vickers dengan beban indentasi 200 gf, dan waktu indentasi selama 5 detik. Bentuk struktur mikro potongan melintang dilihat menggunakan mikroskop optis. Berdasarkan hasil uji kekerasan didapatkan bahwa terjadi penurunan kekerasan seiring dengan penambahan temperatur annealing. Hasil pengamatan struktur mikro juga menunjukkan perubahan struktur mikro disebabkan oleh penambahan temperatur annealing.

Annealing is a heat treatment process for the softening metallic materials, especially plain carbon steels. Based on case study was finded that thrust washer differential on the dump truck unit-machine model CWB6BLLDN2 fell up failure. Failure of component was caused by impack of gear differential on differential case. The cracking of thrust washer was effected by the characteristic of materials which low resistance to impack load. Variation temperatures of annealing process are used by 825 °C, 875 °C, 925 °C, and 975 °C. Furthermore, cooling methode that been used is cooling on furnace. Hardness test is used by Vickers hardness test with indentation load of 200 gf, and indentation time of 5 s. Cross section of microstructure is examined by optical microscope. Based on hardness test, the hardness is decrease by increasing of annealing temperature. Observation of microstructure shown changes on microstructure that been caused by increasing of annealing temperature.

Keyword : Annealing, hardness, microstructure, thrust washer differential

Nilai Properti

: Wahyu Anhar, S.T., M.Eng.

: Patria Rahmawanti, S.Psi., M.MPd, Psikologi

:

: Politeknik Negeri Balikpapan

: Alat Berat

: 2017

: Indonesia


 

Download Full Text